牌号简介 About |
---|
高性能热塑性材料,30%碳纤维增强聚醚醚酮(PEEK),半结晶,注塑和挤压用颗粒,标准流程,符合FDA食品接触标准,颜色为黑色。在静态或动态系统中用于更高强度和刚度的应用。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour black. Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
产品描述 Product Description
厂家:英国威格斯 Victrex
类别:PEEK
颜色:黑色
加工条件:挤出,注射成型 Extrusion,Injection Molding
性能特点: 半结晶; 耐磨; 机械强度好; 耐化学性; 食品接触; 低摩擦系数; 易流动; Good wear resistance,Good liquidity,Food contact compliance,Solvent resistance,Hypocrystalline,Low coefficient of friction,Good Rigidity
填料:碳纤维 30
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
88 | ISO 868 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
28000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
265 | MPa | ISO 527-2 |
断裂,125℃ Fracture, 125 ℃ |
160 | MPa | ISO 527-2 |
断裂,175℃ Fracture, 175 ℃ |
85.0 | MPa | ISO 527-2 |
断裂,275℃ Fracture, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
玻璃化转变温度 Glass transition temperature |
ISO 11357-2 | ||
-- -- |
℃ | ISO 11357-2 | |
-- -- |
℃ | ISO 11357-2 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
MD MD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
相对温度指数 Relative temperature index |
|||
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D4496 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
毒性 toxicity |
NES 713 | ||
CO content CO content |
NES 713 | ||
CO2 content CO2 content |
NES 713 | ||
Total gases Total gases |
NES 713 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 Spiral flow length |
Internal Method | ||
-- -- |
cm | Internal Method | |
-- -- |
cm | Internal Method | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 392°F, 熔体温度: 743°F |
4 1 mm |
5 3 mm |
6 395°C nozzle, 200°C tool |
7 Onset |
8 Midpoint |
9 Average |
10 Along flow |
11 1V |
【新闻资讯】查看全部
Proto Labs的3D打印利润猛增29%
2016-08-02 美国制造解决方案供应商Proto Labs同时扩大了在3D打印行业内和3D打印行业外的业务。 该公司之前主要采用注塑成型和数控加工,现在把增材制造整合到他们的生产工艺中。 上周,Proto Labs再次扩大自己的制造服务,宣布在今年晚些时候将把Concept Laser的LaserCUSING技术引入到自己新的 77000平方英尺的工厂里,提供给客户的服务数量也在继续增加。 Proto Labs第二季度的收入为7500万美元,同比 |
Proto Labs的3D打印利润猛增29% 美国制造解决方法经销商Proto Labs另外扩张了在三维打印行业内和三维打印行业外的业务流程。 该企业以前关键选用注塑工艺和数控车床加工,如今把增材制造融合到她们的生产工艺流程中。 上星期,Proto Labs再度扩张自身的生产制造服务,公布在2020年晚些时候将把Concept Laser的LaserCUSING技术性引入到自身新的 77000平方米的工厂里,出示给顾客的服务总数也在再次提升。 Proto Labs第二季度的收益为7500万美金,同比增长率17%,在其中480万美金的收益来源于Proto Labs在2015年回收的法国企业 Alphaform。 三维打印服务为她们产生的收益达到910万美金(在其中210万美金来源于Alphaform),同比增长率29%。与这种提高产生迥然不同的是,在南美洲的注塑工艺和数控车床加工业务流程欠缺提高。 "在三维打印不断的强悍提高、我们在欧州销售市场的整体实力和来源于Alphaform的奉献的驱动器下,大家第二季度财政总收入的提高十分牢固。"Proto Labs的首席战略官CEO Vicki Holt说,"大家很高兴见到该季度来源于欧州销售市场的收益提高了24%,而在日本,大家则获得了46%的同比增长率。在南美洲,注塑工艺和数控车床加工业务流程的提高比预估的要低,这关键是由于美国工业是社会经济发展的变缓和贸易业的山体滑坡 来源于:塑料新闻我国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 碳纤增强PEEK在飞机电气部件上的运用
- 2019-01-25 0
- VICTREX® PEEK 450CA30为高性能热塑性材料,填充30%碳纤维增强聚醚醚酮(PEEK)。半结晶,注塑和挤压用颗粒,标准流程,符合FDA食品接触标准,颜色为黑色。在静态或动态系统中用于更高强度和刚度的应用。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应
- 阅读全文
碳纤增强PEEK在飞机电气部件上的运用
1-符合AMS美国宇航材料规范标准
2-跟钛合金和镁合金部件相比具有轻量化的优势
3-部件结构设计简单,能够标准化大批量生产
4-与相同性能的金属相比能减少重量,节约成本
5-收缩率很低,必须保证尺寸的稳定性
6-抗冲击强度高,具有良好的机械性能
2-跟钛合金和镁合金部件相比具有轻量化的优势
3-部件结构设计简单,能够标准化大批量生产
4-与相同性能的金属相比能减少重量,节约成本
5-收缩率很低,必须保证尺寸的稳定性
6-抗冲击强度高,具有良好的机械性能
收起
抱歉!暂无数据。