MonoSol® AF A200是一种基于聚乙烯醇的热塑性薄膜,可溶于热水,使用Monosol AF的专有吹塑薄膜技术制造。MonoSol® AF A200是一种典型的聚乙烯醇热水溶性薄膜。在60℃以上,经搅拌可溶解。它具有有限的冷湿强度,主要用于医院洗衣袋,其中大部分亚麻布是干的。它也可用于某些化学部分包装应用的VFFS包装机械,其中包装被置于60°C以上的水和搅拌环境中。可用厚度范围为20微米(0.8密耳)至80微米(3.1密耳)。 MonoSol AF A200 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF A200 is a typical grade of PVOH hot water-soluble film. It is soluble above 60°C with agitation. It has limited cold wet strength and is primarily used for hospital laundry bags where the bulk of the linen is dry. It can also be used on some VFFS machinery for delivery system applications where the film is being put into an environment with water above 60°C with agitation. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
含水量 water content 2 |
|||
23℃ 23℃ 2 |
6.7 | % | |
可溶性 solubility 3 |
|||
Disintegration:60℃,20.0 µm Disintegration:60℃,20.0 µm |
1.0 | sec | |
Disintegration:70℃,20.0 µm Disintegration:70℃,20.0 µm |
1.0 | sec | |
Dissolution:60℃,20.0 µm Dissolution:60℃,20.0 µm |
430.0 | sec | |
Dissolution:70℃,20.0 µm Dissolution:70℃,20.0 µm |
300.0 | sec | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
薄膜厚度 film thickness |
|||
割线模量 Secant modulus |
ASTM D882 , ISO 527-3 | ||
10%,MD:20 µm 10%,MD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
100%,MD:20 µm 100%,MD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
10%,TD:20 µm 10%,TD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
100%,TD:20 µm 100%,TD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
拉伸强度 tensile strength |
|||
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,20 µm MD,20 µm |
MPa | ISO 527-3 | |
TD,20 µm TD,20 µm |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ASTM D882 , ISO 527-3 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 , ISO 527-3 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 , ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709,DIN 53433 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
MD:20 µm MD:20 µm |
N | ISO 6383-2 | |
TD:20 µm TD:20 µm |
N | ISO 6383-2 | |
用量 dosage |
|||
20.0 µm 20.0 µm |
m²/kg | ASTM D4321 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Distilled Water (MSTM 205) |
3 50%RH |
【新闻资讯】查看全部
聚碳酸酯业务为何引得多家上市公司争相介入?
2016-01-15 今年以来,鲁西化工、烟台万华、江山化工这三家化工类上市公司已经或计划拓展高端塑料--聚碳酸酯(PC)业务。在传统大宗化工产品产能过剩的背景下,企业进入高端石化领域,凸显传统化工企业转型升级的趋势。 作为高端石化产品,聚碳酸酯(PC)是五大工程塑料之一,具有良好光学性能、机械性能、电绝缘性能,广泛应用于建筑材料、电子电气、汽车材料等行业。近年来需求增长速度快,长期需要大量进口。 咨询数据显示,中国已成为全球重要的PC市场,2014年净进口量约126万吨。对外依 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |